This investigation demonstrated 2.1 wt% tungsten drastically reduced the kinetics of tertiary phase precipitation in 25Cr super duplex stainless steels. The slow kinetics resulted in a better overall pitting corrosion resistance.
Uncategorized
Hydrogen Embrittlement of Industrial Components: Prediction, Prevention, and Models – Publication
Hydrogen embrittlement is a common, dangerous, and poorly understood cause of failure in many metal alloys. This article presents a model based on the correlation of mechanical properties to scanning electron microscopy fractography analysis of fracture surfaces in the presence of simultaneously active hydrogen embrittlement micro-mechanisms.