This presentation gave at CORROSION 2017, introduces the concept of cathodic protection by distributed sacrificial anodes (DSA), a promising new approach to optimizing external corrosion protection..
This lecture describes various materials selection and corrosion control strategies for subsea oil and gas production systems. A brief discussion on carbon and low alloy steels as well as corrosion resistance alloys is presented alongside fundamental corrosion concepts.
Does tungsten in super duplex stainless steel improve localized corrosion resistance?
In this presentation, the pitting and crevice corrosion resistance of super duplex stainless steels with different tungsten contents was analyzed using various electrochemical techniques.
The work was presented at the 16th Nordic Corrosion Conference.
Do magnesium alloys suffer environmentally assisted cracking?
In this work, presented at CORROSION 2014, we investigated the hydrogen embrittlement and stress corrosion cracking of magnesium alloy AZ31B in chloride solutions.
How can we prevent cracking of high strength low alloy steels when exposed to hydrogen? Take a look at my presentation at the 2015 Robust Materialvalg i Oljeindustrien conference.
This work was presented at NACE International CORROSION 2015 "Mechanisms of Localized Corrosion" symposium.
A link to the final presentation is included.