• Skip to primary navigation
  • Skip to main content

About Corrosion

All about corrosion science and engineering

  • Home
  • Announcements
  • Sections
    • Fundamentals
      • HowTos
      • Electrochemistry
      • Thermodynamics
      • Kinetics
      • Localized corrosion
      • Stress corrosion cracking
      • Cathodic protection
      • Carbon dioxide
    • Physical Metallurgy
    • Low alloy steels
    • Corrosion Resistant Alloys
      • Stainless steels
      • Nickel Alloys
  • Library
    • Lectures
    • Journal Articles
    • Conference Papers
    • Presentations
    • Abstracts
    • Definitions
    • Equations
    • Standards
    • Videos
    • Tables
  • Ref Convert
  • OpenLab!

Hydrogen-Induced Stress Cracking of Swaged Super Duplex Stainless Steel Subsea Components

August 1, 2019 by Mariano Iannuzzi

Overview

Together with my PhD student Sofia Hazarabedian and my colleagues Andy Viereckl, Garry Leadbeater, Zak Quadir, Vlad Golovanevskiy, Skjalg Erdal, and Paul Georgeson, we recently published a comprehensive root-cause analysis and thorough hydrogen-induced stress cracking investigation of swaged 25Cr super duplex connectors.

This work focuses on two connectors used in subsea production equipment, both showing a single longitudinal crack in a swaged section. The components were manufactured from UNS S32760, a 25 wt% Cr SDSS with a specified minimum yield strength (SMYS) of 550 MPa (80 ksi). The external surface of the connectors was exposed to a restricted flow of seawater and the components were in both electrical and electrolytic contact with a larger carbon steel subsea structure. The parts were subjected to CP, and substantial accumulations of calcareous deposits were found upon initial inspection. The cracking extended along the swaged part of the component and the visual appearance suggested cleavage fracture and, hence, the possibility of a Hydrogen induced stress cracking (HISC) failure. A comprehensive materials characterization that included positive material identification, fractography, microstructure analysis, microhardness mapping, total hydrogen concentration, as well as pitting corrosion and tensile testing was undertaken to address the three contributing factors of an environmentally assisted failure, namely, (i) the material and manufacturing routes, (ii) the presence of hydrogen, and (iii) the possibility of stress raiser and design considerations. The main findings of the analysis are presented herein.

Hydrogen induced stress cracking of a swaged UNS S32760 subsea connector.

Why is it important?

HISC is the Achilles’ heel of duplex and super duplex stainless steels. In this investigation, we demonstrate the detrimental effects of both cold work (swaging) and anisotropic microstructures on HISC resistance. We believe the findings challenge the validity of the present form of DNV-GL RP F112 as a method to reduce HISC risks. 

Abstract

A recent subsea failure of two subsea connectors made of UNS S32760, a 25 wt% Cr super duplex stainless steel, led to an extensive root cause failure analysis. The components showed a single longitudinal crack along a swaged section, which arrested toward its thicker end. The brittle nature of the fracture surface, calcareous deposits on the component, and exposure to cathodic protection suggested hydrogen-induced stress cracking—a form of environmentally assisted cracking—as a plausible failure mechanism. Thus, the three causative factors promoting hydrogen-induced stress cracking, namely, a susceptible microstructure, a hydrogen bearing environment, as well as sufficiently high applied and residual stresses in the material were the focus of this investigation. This work details the material characterization work and presents a possible failure mechanism. The results showed that the failure developed from a combination of factors, typical for hydrogen-induced stress cracking. The measured hydrogen content in parts of the material exceeded 40 ppm, more than an order of magnitude higher than what is normally expected in super duplex stainless steels. Additionally, a highly anisotropic, coarse microstructure was observed, which in combination with the introduced cold-work from the swaging process and potential stress raisers from design and machining could have facilitated crack initiation, ultimately leading to the failure of the component. This hypothesis was reinforced by the presence of secondary cracks along the main, brittle fracture surface. Furthermore, mechanical testing results showed a detrimental effect on the material’s properties due to the presence of residual hydrogen and the swaging operation.

Citation

M. Sofia Hazarabedian, Andreas Viereckl, Zakaria Quadir, Garry Leadbeater, Vladimir Golovanevskiy, Skjalg Erdal, Paul Georgeson, Mariano Iannuzzi, Hydrogen-Induced Stress Cracking of Swaged Super Duplex Stainless Steel Subsea Components, CORROSION. 2019;75(7):824-838. https://doi.org/10.5006/3192.

Download

Copyright

The article has been published as OpenAccess, distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.

Badges

Filed Under: Environmentally Assisted Cracking, hisc, Hydrogen Embrittlement, Journal Articles, Physical Metallurgy Tagged With: hisc, hydrogen, hydrogen embrittlement, stainless steels, super duplex stainless steels

Professor | Director Curtin Corrosion Centre
Chevron & Woodside Chair in Corrosion | Curtin University
Adjunct Professor
Norwegian University of Science and Technology (NTNU)

  • About
  • Contact Me
  • Subscribe
  • Ref Convert

Copyright © 2022 · Mariano Iannuzzi · WordPress · Log in