• Skip to primary navigation
  • Skip to main content

About Corrosion

All about corrosion science and engineering

  • Home
  • Announcements
  • Sections
    • Fundamentals
      • HowTos
      • Electrochemistry
      • Thermodynamics
      • Kinetics
      • Localized corrosion
      • Stress corrosion cracking
      • Cathodic protection
      • Carbon dioxide
    • Physical Metallurgy
    • Low alloy steels
    • Corrosion Resistant Alloys
      • Stainless steels
      • Nickel Alloys
  • Library
    • Lectures
    • Journal Articles
    • Conference Papers
    • Presentations
    • Abstracts
    • Definitions
    • Equations
    • Standards
    • Videos
    • Tables
  • Ref Convert
  • OpenLab!

Use of electrochemical techniques to determine the effect of Sigma phase (σ-phase) precipitation on a 25Cr Super Duplex Stainless Steel — Presentation

February 22, 2015 by Mariano Iannuzzi

This work was presented at the NACE International CORROSION 2015 “Mechanisms of Localized Corrosion” symposium sponsored by the STG60 – Corrosion Mechanisms.

By: Mariano Iannuzzi

Coauthors: Monika Næss and Prof. Roy Johnsen.

Abstract

Corrosion resistant alloys (CRA) for subsea pressure-retaining components must be compatible with production fluids and resistant to pitting and crevice corrosion in seawater. Whereas materials selection for production environments is governed by well-established standards such as ISO 15156, debate still exists as of how to determine the seawater corrosion resistance of CRA.

While most industry specifications rely on the ASTM G48 standard to determine localized corrosion resistance, for duplex and super duplex stainless steels there is no consensus on the surface finish before testing and test temperature. Moreover, it is unclear whether existing procedures are sensitive enough to determine the onset of deleterious phases such as σ-phase and chromium nitrides.

The objective of this investigation was to quantify the seawater pitting corrosion resistance of a 25-wt%Cr super duplex stainless steel and its correlation with: i) alloy’s microstructure and ii) surface finish before testing. Cyclic potentiodynamic polarization (CPP) testing was used to determine the effect of different σ-phase volume fractions on corrosion response. CPP tests were conducted at various temperatures, ranging from 20 to 90°C, to determine the effect of deleterious phases on critical pitting and crevice temperatures (CPT and CCT, respectively). CPP results were compared with reported values based on ASTM G48 method D, ASTM G150, and zero resistance amperometry.

Final Presentation

The final version of the presentation can be downloaded here.

Conference paper

The conference paper can be downloaded HERE.

Filed Under: Conferences, Critical potentials, Localized corrosion, Presentations Tagged With: CORROSION/15, CRA, critical pitting temperature, localized corrosion, materials selection, Oil&Gas, PREN, sdss, seawater, sensitization, sigma phase, stainless steels, Subsea

Professor | Director Curtin Corrosion Centre
Chevron & Woodside Chair in Corrosion | Curtin University
Adjunct Professor
Norwegian University of Science and Technology (NTNU)

  • About
  • Contact Me
  • Subscribe
  • Ref Convert

Copyright © 2022 · Mariano Iannuzzi · WordPress · Log in